本文以水合氯化镁、工业氨水为原料制备出了低硼含量的纯度 >99%的氢氧化镁和氧化镁。利用差热 -热重 (DTA- TG)、X-射线衍射 (XRD)、透射电子显微镜 (TEM)等手段 ,对氢氧化镁的热稳定性、相结构、表观状态以及脱水动力学参数进行了分析。结果为 :氢氧化镁以束状纤维和片状粉末共存 ,在 6 2 3K基本完成脱水反应生成氧化镁 ,其脱水反应的表观活化能 E为135 .4 k J· mol-1,指前因子 A为 5 .15× 10 10 ,反应级数 n为 1.10
Abstract：Samples of magnesium hydroxide with low boron content(about 0.002 05 w%) were prepared from MgCl 2·6H 2O and NH 3·H 2O. DTA TG, XRD and TEM were employed to characterize the samples. The decomposition kinetic parameters of magnesium hydroxide were studied by the Kissinger method. The results show that the sample is a mixture of bunchy fibres and sheet form powder, it decomposes to magnesium oxide at about 623K, and the activation energy, the pre exponential factor, and the reaction order are 135.4kJ·mol -1 , 5.15×10 10 and 1.10 respectively.
[1] 郭如新.氢氧化镁在工业废水处理中的应用.[J]工业水处理,2000,20(2):1～4
[2] 李克民,张 莉.氨法制取氢氧化镁阻燃剂实验报告.[J]无机盐工业,2001,33(2):14～16
[3] 徐旺生,宣爱国.阻燃剂型氢氧化镁生产新工艺研究.[J]无机盐工业,2001,33(1):13～15
[4] 李玉玺.氢氧化镁阻燃剂发展前景广阔.[J]海湖盐与化工,2000,29(1):40
[5] 胡庆福,刘鸿雁,王金阁,等.一步法制备氢氧化镁阻燃剂新工艺.[J]现代化工,1998(3):23～24
[6] 曹 霞,陈秀萍.浅谈氢氧化镁法脱硫技术.[J]有色冶金设计与研究,2000,21(1):47～51
[7] 郑荣光,王 芳.氢氧化镁处理含铅废水的研究.[J]无机盐工业,2000,32(1):26～28
[8] 方裕勋,罗 新.卤水—白云石法氢氧化镁沉淀过程试验和研究.[J]无机盐工业,1998,30(2):9～12
[9] 王正洲,范维澄,瞿保钧,等.含氢氧化镁的阻燃硅烷交联聚乙烯.[J]功能高分子学报,2000,13(1):77～80
[10] 翟学良.氢氧化镁热分解行为与机理研究.[J]矿产综合利用,2000(3):12～15
[11] 中华人民共和国国家标准GB603-77.制剂及制品制备方法.[S]
[12] 中华人民共和国国家标准GB672-88.化学试剂—氯化镁.[S]
[13] 苏培基.工业氢氧化镁化工行业标准简介.[J]化工标准.计量.质量,2001,4:3～4
[14] 中华人民共和国国家标准GB9857-88,化学试剂氧化镁.[S]
[15] 中华人民共和国行业标准HG/T2573-94.工业氧化镁.[S]
[16] 蔡正千.热分析.[M]北京:高等教育出版社,1993:113～115
[17] (日)神户博太郎编,刘振海等译.热分析.[M]北京:化学工业出版社,1982:5
基本信息:
DOI：10.16441/j.cnki.hdxb.2002.05.019
中图分类号:X703
引用信息:
[1]高荣杰,冯丽娟,杜敏,宁滨,梁丽.低硼氢氧化镁的制备及热分解动力学参数[J].青岛海洋大学学报(自然科学版),2002(05):789-794.DOI:10.16441/j.cnki.hdxb.2002.05.019.
2002-10-30
2002-10-30